ASTM A420 WPL6 Grade is associated with ASTM A420 for pipe fittings manufactured of Wrought Carbon Steel.

ASTM A420/A420M-07 Standard Specification for Piping Fittings of Wrought Carbon Steel and Alloy Steel for Low-Temperature Service. WPL6 is a normalized grade of carbon steel that has been Charpy Impact tested at -50 degree F for use in low temperature service. See Also ASTM A333 Grades 1 and 6 (for pipe) and A350 LF2 for flanges.

ASTM A420 WPL6 Elbow after complete quality and performance measure inspection. These are widely appreciated for excellent quality, corrosion abrasion and high tensile strength with long life service.

Materials shall consist of forgings, bars, plates, seamless or fusion welded tubular products with filler metal added, and shall be produced by open-hearth, basic-oxygen, or electric-furnace process. Forging or forming operations shall be performed by one or a combination of two or more of the following procedures: hammering, pressing, piercing, extruding, upsetting, working, bending, fusion-welding, or machining. All welding shall be completed prior to the austenitizing heat treatment, which shall be executed in the normalized, normalized and tempered, annealed, or quenched and tempered conditions. Steel specimens shall conform to required values of chemical composition, tensile strength, yield strength, elongation, wall thickness, and Charpy V-notch impact value. All fusion-welded butt joints shall undergo radiographic examination, while hydrostatic testing of fittings is not required in this specification. Repair welding shall be permissible for parts made to dimensional standards.

Chemical Composition (%) of ASTM A420 WPL6

GENERAL NOTE:
 All values are maximum unless otherwise indicated.

NOTES:
(1) For each reduction of 0.01% C below 0.30%, an increase of 0.05% Mn above 1.06% will be permitted, up to a maximum of 1.35%.
 (2) Fittings made from forgings may have 1.35% max Mn.

Mechanical properties of ASTM A420 WPL6